4P-NPD ultra thin-films as efficient exciton blocking layers in DBP/C70 based organic solar cells

Publikation: Forskning - peer reviewTidsskriftartikel

Links

DOI

Vis graf over relationer

Exciton blocking effects from ultra thin layers of N,N'-di-1-naphthalenyl-N,N'-diphenyl [1,1':4',1'':4'',1'''-quaterphenyl]-4,4'''-diamine (4P-NPD) was investigated in small molecule based inverted Organic Solar Cells (OSCs) using Tetraphenyldibenzoperiflanthene (DBP) as the electron donor material and fullerene (C70) as the electron acceptor material. The short-circuit current density (Jsc) and PCE of the optimized OSCs with 0.7 nm thick 4P-NPD were approx. 16 % and 24 % higher, respectively, compared to reference devices without exciton blocking layers. Drift diffusion based device modeling was conducted to model the full Current density – Voltage (JV) characteristics and EQE spectrum of the OSCs, and photoluminescence measurements was conducted to investigate the exciton blocking effects with increasing thicknesses of the 4P-NPD layer. Importantly, coupled optical and electrical modeling studies of the device behaviors and exciton generation rates and densities in the active layer for different 4P-NPD layer thicknesses were conducted, in order to gain a complete understanding of the observed increase in PCE for 4P-NPD layer thicknesses up to 1 nm, and the observed decrease in PCE for layer thicknesses beyond 1 nm. This work demonstrates a route for guiding the integration of exciton blocking layers in organic solar cell devices.
OriginalsprogEngelsk
Artikelnummer385101
TidsskriftJournal of Physics D: Applied Physics
Vol/bind50
Tidsskriftsnummer38
Antal sider8
ISSN0022-3727
DOI
StatusUdgivet - 2017